Formation of low K material utilizing process having readily cleaned by-products

ABSTRACT

Nano-porous low dielectric constant films are deposited utilizing materials having reactive by-products readily removed from a processing chamber by plasma cleaning. In accordance with one embodiment, an oxidizable silicon containing compound is reacted with an oxidizable non-silicon component having thermally labile groups, in a reactive oxygen ambient and in the presence of a plasma. The deposited silicon oxide film is annealed to form dispersed microscopic voids or pores that remain in the nano-porous silicon. Oxidizable non-silicon components with thermally labile groups that leave by-products readily removed from the chamber, include but are not limited to, limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, 2,5 Norbornadiene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene.

CROSS-REFERENCE TO RELATED APPLICATION

The instant nonprovisional patent application claims priority from provisional patent application No. 60/645,082, filed Jan. 18, 2005 and incorporated herein by reference for all purposes.

BACKGROUND OF THE INVENTION

One of the primary steps in the fabrication of modem semiconductor devices is the formation of metal and dielectric films on a substrate by chemical reaction of gases. Such deposition processes are referred to as chemical vapor deposition or CVD. Conventional thermal CVD processes supply reactive gases to the substrate surface where heat-induced chemical reactions take place to produce a desired film. The high temperatures at which some thermal CVD processes operate can damage device structures having layers previously formed on the substrate. A preferred method of depositing metal and dielectric films at relatively low temperatures is plasma-enhanced CVD (PECVD) techniques such as described in U.S. Pat. No. 5,362,526, entitled “Plasma-Enhanced CVD Process Using TEOS for Depositing Silicon Oxide”, which is incorporated by reference herein. Plasma-enhanced CVD techniques promote excitation and/or disassociation of the reactant gases by the application of radio frequency (RF) energy to a reaction zone near the substrate surface, thereby creating a plasma of highly reactive species. The high reactivity of the released species reduces the energy required for a chemical reaction to take place, and thus lowers the required temperature for such PECVD processes.

Semiconductor device geometries have dramatically decreased in size since such devices were first introduced several decades ago. Since then, integrated circuits have generally followed the two year/half-size rule (often called Moore's Law), which means that the number of devices that will fit on a chip doubles every two years. Today's fabrication plants are routinely producing devices having 0.351 μm and even 0.25 μm feature sizes, and tomorrow's plants soon will be producing devices having even smaller geometries.

In order to further reduce the size of devices on integrated circuits, it has become necessary to use conductive materials having low resistivity and insulators having low k (dielectric constant<2.5) to reduce the capacitive coupling between adjacent metal lines. Liner/barrier layers have been used between the conductive materials and the insulators to prevent diffusion of byproducts such as moisture onto the conductive material as described in International Publication Number WO 99/41423, published on Aug. 17, 1999. For example, moisture that can be generated during formation of a low k insulator readily diffuses to the surface of the conductive metal and increases the resistivity of the conductive metal surface. A barrier/liner layer formed from organosilicon or organosilane nitride materials can block the diffusion of the byproducts. However, the barrier/liner layers typically have dielectric constants that are greater than about 2.5, and the high dielectric constants result in a combined insulator that may not significantly reduce the dielectric constant.

FIG. 1A-1E illustrates a three-layer deposition PECVD process for depositing a PECVD lining layer 2 of the oxidized organosilane or organosiloxane polymer as described in International Publication Number WO 99/41423. The lining layer 2 acts as an isolation layer between a subsequent layer 7 and the underlying substrate surface 6 and metal lines 8, 9, 10 formed on the substrate surface. The layer 7 is capped by a PECVD capping layer 12 of the oxidized organosilane or organosiloxane polymer. The PECVD process deposits a multi-component dielectric layer, wherein an carbon containing silicon dioxide (SiO₂) is first deposited on the patterned metal layer having metal lines 8, 9, 10 formed on substrate 6.

Referring to FIG. 1A, the PECVD lining layer 2 is deposited by the plasma enhanced reaction of an organosilane or organosiloxane compound such as methylsilane, CH₃SiH₃, and an oxidizing gas such as N₂O in the presence of an inert gas, such as argon, at a temperature of approximately −20° C. to 40° C. The oxidized organosilane or organosiloxane layer is then cured. The deposited PECVD lining layer 2 (at about 2000 Å per minute) has improved barrier characteristics for the subsequent deposition of the layer 7 shown in FIG. 1B. The lining layer obtained from methylsilane has sufficient C—H bonds to be hydrophobic, and is an excellent moisture barrier. A low K dielectric layer 7 is then deposited on the liner layer 2 by the reaction of a silane compound and hydrogen peroxide (H₂O₂) at a temperature below 200° C. at a pressure of about 0.2 to about 5 Torr during deposition of the layer 7. The layer 7 may be partially cured as shown in FIG. 1C to remove solvents such as water prior to deposition of a cap layer 12 as shown in FIG. 1D. Curing is performed by pumping down a reaction under an inert gas atmosphere under 10 Torr.

Conventional liner layers, such as silicon nitride (SiN), have higher dielectric constants than silicon oxides, and the combination of low k dielectric layers with high k dielectric liner layers provides little or no improvement in the overall stack dielectric constant and capacitive coupling. Referring to FIG. 1D, after deposition of the layer 7, an optional capping layer 12 may be deposited on the low k dielectric layer 7 by the plasma enhanced reaction of an organosilane or organosiloxane compound and an oxidizing gas such as N₂O. Referring to FIG. 1E, after deposition of the capping layer, if any, the deposited layers are cured in a furnace or another chamber to drive off remaining solvent or water. The capping layer 12 is also an oxidized organosilane or organosiloxane film that has good barrier properties and has a dielectric property of about 3.0. Both the liner layer 2 and the cap layer 12 have a dielectric constant greater than 3.0 and the high dielectric constant layers substantially detract from the benefit of the low k dielectric layer 7.

As devices get smaller, liner layers and cap layers having relatively high dielectric constants contribute more to the overall dielectric constant of a multi-component dielectric layer. Additionally, the smaller device geometries result in an increase in parasitic capacitance between devices. Parasitic capacitance between metal interconnects on the same or adjacent layers in the circuit can result in crosstalk between the metal lines or interconnects and/or resistance-capacitance (RC) delay, thereby reducing the response time of the device and degrading the overall performance of the device. The effects of parasitic capacitance between metal interconnects on the same or adjacent layers in the circuit is especially of concern as the current state of the art circuits can employ 4 to 5 levels of interconnection, while next generation devices may require 6, 7, or possibly 8 levels of interconnection.

Lowering the parasitic capacitance between metal interconnects separated by dielectric material can be accomplished by either increasing the thickness of the dielectric material or by lowering the dielectric constant of the dielectric material. Increasing the thickness of the dielectric materials, however, does not address parasitic capacitance within the same metallized layer or plane. As a result, to reduce the parasitic capacitance between metal interconnects on the same or adjacent layers, one must change the material used between the metal lines or interconnects to a material having a lower dielectric constant than that of the materials currently used, i.e., k≈3.0.

Therefore, there remains a need for dielectric layers having dielectric constants below about 2.5 with good adhesion properties.

SUMMARY OF THE INVENTION

Nano-porous low dielectric constant films are deposited utilizing materials having reactive by-products readily removed from a processing chamber by plasma cleaning. In accordance with one embodiment, an oxidizable silicon containing compound is reacted with an oxidizable non-silicon component having thermally labile groups, in a reactive oxygen ambient and in the presence of a plasma. The deposited silicon oxide film is annealed to form dispersed microscopic voids or pores that remain in the nano-porous silicon. Oxidizable non-silicon components with thermally labile groups that leave by-products readily removed from the chamber, include but are not limited to, limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, 2,5-Norbornadiene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene.

An embodiment of a method in accordance with the present invention for generating a low dielectric constant film, comprising, disposing a substrate within a processing chamber, providing an oxidizable silicon containing compound into the processing chamber, and providing a carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, bicyclo-hepa-diene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene into the processing chamber. The oxidizable silicon containing compound and the carbon containing precursor are reacted with an oxidizing gas to form a carbon-doped dielectric film over the substrate, and the substrate is annealed to create pores in the carbon-doped dielectric film.

An embodiment of a dielectric structure in accordance with the present invention for a semiconducting device, comprises, a carbon-doped silicon oxide feature formed by the oxidative reaction between an oxidizable silicon containing compound and a carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, bicyclo-hepa-diene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene followed by annealing to create pores therein.

An embodiment of an apparatus for depositing a carbon-doped low K dielectric film, comprises, a chamber enclosing a substrate support, a heat source in thermal communication with the chamber, an oxidizable silicon containing component source in fluid communication with the chamber, and a carbon-containing precursor source in fluid communication with the chamber. An oxidant source is in fluid communication with the chamber, and a host processor is in communication with the chamber. A computer readable storage medium has a computer readable program embodied therein for directing operation of the processor to cause the oxidizable silicon containing component to flow into the processing chamber, to cause the carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, bicyclo-hepa-diene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene to flow into the processing chamber, to cause the oxidant to flow into the chamber and react with the oxidizable silicon containing compound and the carbon containing precursor to form a carbon-doped dielectric film over a substrate supported by the support, and to cause the heat source to anneal the substrate to create pores in the carbon-doped dielectric film.

These and other objects and features of the present invention and the manner of obtaining them will become apparent to those skilled in the art, and the invention itself will be best understood by reference to the following detailed description read in conjunction with the accompanying drawings.

A further understanding of embodiments in accordance with the present invention can be made by way of reference to the ensuing detailed description taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1E are schematic diagrams of dielectric layers deposited on a substrate by the processes known in the art.

FIG. 2 is a cross-sectional diagram of an exemplary CVD reactor configured for use according to the present invention.

FIG. 3 is a schematic diagram of a remote microwave chamber for dissociation of process gases prior to entering the reactor of FIG. 2.

FIG. 4 is a flowchart of a process control computer program product used in conjunction with the exemplary CVD reactor of FIG. 2.

FIG. 5 is a flow chart illustrating steps undertaken in depositing liner and cap layers in a deposition process according to one embodiment of the present invention.

FIGS. 6A-6E are schematic diagrams of the layers deposited on a substrate by the process of FIG. 5.

FIG. 7 is a cross sectional view showing a dual damascene structure comprising the silicon oxide layers of the present invention.

FIGS. 8A-8H are cross sectional views showing one embodiment of a dual damascene deposition sequence of the present invention.

FIGS. 9A-B show photographs taken of a 300 mm BDIIx chamber cleaned with remote plasma after running a nano-porous film deposition clean process.

FIGS. 9C-D plots infrared (FT-IR) absorbance spectra for the two residue types shown in FIGS. 9A-B.

FIGS. 10A-O show chemical structures of examples of readily cleaned organic compounds suitable for use in forming nano-porous layers by chemical vapor deposition (CVD).

DESCRIPTION OF THE SPECIFIC EMBODIMENTS

Deposition of nano-porous low dielectric constant films in accordance with embodiments of the present invention utilizes materials having reactive by-products readily removed from a processing chamber by plasma cleaning. In accordance with one embodiment, an oxidizable silicon containing compound is reacted with an oxidizable non-silicon component having thermally labile groups, in an ambient containing reactive oxygen and in the presence of a plasma. The deposited silicon oxide film is annealed to form dispersed microscopic voids that remain in the nano-porous silicon. Oxidizable non-silicon components leaving by-products readily cleaned from the chamber, include but are not limited to, limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, 2,5-Norbornadiene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene.

U.S. Pat. No. 6,541,367, incorporated by reference herein for all purposes, describes a method for depositing a nano-porous silicon oxide layer having a low dielectric constant. The nano-porous silicon oxide layer is produced by plasma enhanced (PECVD) or microwave enhanced chemical vapor deposition of a silicon/oxygen containing material that optionally contains thermally labile organic groups, and by controlled annealing of the deposited silicon/oxygen containing material to form microscopic gas pockets that are uniformly dispersed in a silicon oxide layer. The relative volume of the microscopic gas pockets to the silicon oxide layer is controlled to preferably maintain a closed cell foam structure that provides low dielectric constants after annealing. The nano-porous silicon oxide layers will have dielectric constants less than about 2.5, preferably less than about 2.0.

The silicon/oxygen material is chemical vapor deposited by reacting an oxidizable silicon containing compound or mixture comprising an oxidizable silicon component and an unsaturated non-silicon bearing component having thermally liable groups with an oxidizing gas. The oxidizing gases are oxygen (O₂) or oxygen containing compounds such as nitrous oxide (N₂O), ozone (O₃), and carbon dioxide (CO₂), preferably N₂O or O₂.

Oxygen and oxygen containing compounds are preferably dissociated to increase reactivity when necessary to achieve a desired carbon content in the deposited film. RF power can be coupled to the deposition chamber to increase dissociation of the oxidizing compounds. The oxidizing compounds may also be dissociated in a microwave chamber prior to entering the deposition chamber to reduce excessive dissociation of the silicon containing compounds. Deposition of the silicon oxide layer can be continuous or discontinuous. Although deposition preferably occurs in a single deposition chamber, the layer can be deposited sequentially in two or more deposition chambers. Furthermore, RF power can be cycled or pulsed to reduce heating of the substrate and promote greater porosity in the deposited film.

The oxidizable silicon component of the oxidizable silicon containing compound or mixture comprises organosilane or organosiloxane compounds which generally include the structure:

wherein each Si is bonded to at least one hydrogen atom and may be bonded to one or two carbon atoms, and C is included in an organo group, preferably alkyl or alkenyl groups such as —CH₃, —CH₂—CH₃, —CH₂—, or —CH₂—CH₂—, or fluorinated carbon derivatives thereof. When an organosilane or organosiloxane compound includes two or more Si atoms, each Si is separated from another Si by —O—, —C—, or —C—C—, wherein each bridging C is included in an organo group, preferably alkyl or alkenyl groups such as —CH₂—, —CH₂—CH₂—, —CH(CH₃)—, —C(CH₃)₂—, or fluorinated carbon derivatives thereof. Examples of silicon-containing precursors useful in accordance with embodiments of the present invention include, but are not limited to, octamethyl-trisiloxane, 1,1,1,3,5,5,5,-heptamethyl-trisiloxane, 1,3,5-trimethyl-1,3,5-trivinylcyclotrisiloxane, (CH₃)₂SiH)₂O, decamethylcyclopentasiloxane, 2,4,6,8-tetramethylcyclotetrasiloxane, octamethylcyclotetrasiloxane, methyldiethoxysilane, trimethyl-silane, and triethoxymethyl-silane.

Preferred organosilane and organosiloxane compounds are gases or liquids near room temperature and can be volatilized above about 10 Torr. Suitable silicon containing compounds include: methylsilane, CH₃—SiH₃ dimethylsilane, (CH₃)₂—SiH₂ disilanomethane, SiH₃—CH₂—SiH₃ bis(methylsilano)methane, CH₃—SiH₂—CH₂—SiH₂—CH₃ 2,4,6-trisilaoxane —(—SiH₂—CH₂—SiH₂—CH₂—SiH₂—O—)- (cyclic) cyclo-1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene —(—SiH₂—CH₂—SiH₂—O—)₂-(cyclic) 1,3,5-trisilacyclohexane, —(—SiH₂—CH₂—)₃-(cyclic) 1,3-dimethyldisiloxane, CH₃—SiH₂—O—SiH₂—CH₃ 1,1,3,3-tetramethyldisiloxane (CH₃)₂—SiH—O—SiH—(CH₃)₂ 1,1,5,5-tetramethyltrisiloxane, and (CH₃)₂—SiH—O—SiH₂—O—SiH—(CH₃)₂ 1,1,3,5,5-pentamethyltrisiloxane (CH₃)₂—SiH—O—SiH(CH₃)—O—SiH— (CH₃)₂ and fluorinated carbon derivatives thereof, such as 1,2-disilanotetrafluoroethane. The hydrocarbon groups in the organosilanes and organosiloxane may be partially or fully fluorinated to convert C—H bonds to C—F bonds. Many of the preferred organosilane and organosiloxane compounds are commercially available. A combination of two or more of the organosilanes or organosiloxanes can be employed to provide a blend of desired properties such as dielectric constant, oxide content, hydrophobicity, film stress, and plasma etching characteristics.

When the oxidizable silicon component forms a compound with an unsaturated non-silicon bearing component having thermally liable groups, the organosilane or organosiloxane compound are functional groups possessing both a silicon oxygen bond and a silicon-hydrogen bond. Preferred functional groups having the bonding requirements include: methylsiloxy, and (CH₃—SiH₂—O—) dimethylsiloxy ((CH₃)₂—SiH—O—)

The unsaturated non-silicon bearing component having thermally liable groups has the property of reacting with an plasma-sustained oxidizing environment to form thermally labile molecules that deposit, and which, when subsequently exposed to elevated temperatures, thermally decompose to form volatile species with low boiling points. Decomposition and evolution of the thermally labile group's volatile species from the deposited film will leave voids in the structure, reducing the structure's density. Selectively removing embedded chemically reacted solid material within the deposited film by a thermal process results in low density films which have low dielectric constants. Formation of voids using some compounds such as 2,4,6-trisilaoxane (2,4,6-trisilatetrahydropyran) and cyclo-1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene is achieved during annealing without addition of labile groups by virtue of a non-planar ring structure:

-   1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene, and     —(—SiH₂—CH₂—SiH₂—O—)₂— (cyclic) -   2,4,6-trisilatetrahydropyran, —SiH₂—CH₂—SiH₂—CH₂—SiH₂—O— (cyclic)

The thermally labile organic groups contain sufficient oxygen to form gaseous products when the silicon oxide layer is annealed.

When the oxidizable silicon component forms a compound with an unsaturated non-silicon bearing component having thermally liable groups, preferred thermally labile groups are non-silicon containing multiply unsaturated cycloalkanes (having two or more carbon-carbon double bonds), including heterocyclodialkenes, with oxygen or nitrogen incorporated within the molecular structure, and which generally tend to perform favorably in plasma environments. Preferred labile groups include: Dioxin, C₄H₄O₂, —(—CH═CH—O—CH═CH—O—)—, cyclic Furan, C₄H₄O, —(—CH═CH—CH═CH—O—)—, cyclic Fulvene, C₆H₆, —(—CH═CH—CH═CH—C(CH₂)—)—, cyclic

Oxidizable silicon containing compounds comprising the oxidizable silicon component and the thermally liable groups include: methylsilyl-1,4-dioxinyl ether CH₃—SiH₂—O—(C₄H₃O₂) 2-methylsiloxanyl furan —(—CH═CH—CH═C(O—SiH₂—CH₃)—O—)—, cyclic 3-methylsiloxanyl furan —(—CH═CH—C(O—SiH₂—CH₃)═CH—O—)—, cyclic 2,5-bis(methylsiloxy)-1,4-dioxin —(—CH═C(O—SiH₂—CH₃)—O—CH═C(O—SiH₂—CH₃)—O—)—, cyclic 3,4-bis(methylsiloxanyl) furan —(—CH═C(O—SiH₂—CH₃)—C(O—SiH₂—CH₃)═CH—O—)—, cyclic 2,3-bis(methylsiloxanyl) furan —(—CH═CH—C(O—SiH₂—CH₃)═C(O—SiH₂—CH₃)—O—)—, cyclic 2,4-bis(methylsiloxanyl) furan —(—CH═C(O—SiH₂—CH₃)—CH═C(O—SiH₂—CH₃)—O—)—, cyclic 2,5-bis(methylsiloxanyl) furan —(—C(O—SiH₂—CH₃)═CH—CH═C(O—SiH₂—CH₃)—O—)—, cyclic 1-methylsiloxanylfulvene —(—CH═CH—CH═CH—C(CH(O—SiH₂—CH₃))—)—, cyclic 2-methylsiloxanylfulvene —(—CH═CH—CH═CH—C(CH₂)(O—SiH₂—CH₃)—)—, cyclic 6-methylsiloxanylfulvene —(—C(O—SiH₂—CH₃)═CH—CH═CH—C═CH—)—, cyclic bis(methylsiloxanyl)fulvene (C₆H₄)(O—SiH₂—CH₃)₂, cyclic dimethylsilyl-1,4-dioxinyl ether (CH₃)₂—SiH—O—(C₄H₃O₂), cyclic 2-dimethylsiloxanyl furan —(—CH═CH—CH═C(O—SiH—(CH₃)₂)—O—)—, cyclic 3-dimethylsiloxanyl furan —(—CH═CH—C(O—SiH—(CH₃)₂)═CH—O—)—, cyclic 2,5-bis(dimethylsiloxy)-1,4-dioxin —(—CH═C(O—SiH—(CH₃)₂)—O—CH═C(O—SiH—(CH₃)₂)—O—)—, cyclic 3,4-bis(dimethylsiloxanyl) furan —(—CH═C(O—SiH—(CH₃)₂)—C(O—SiH—(CH₃)₂)═CH—O—)— cyclic 2,3-bis(dimethylsiloxanyl) furan —(—CH═CH—C(O—SiH—(CH₃)₂)═C(O—SiH—(CH₃)₂)—O—)— cyclic 2,4-bis(dimethylsiloxanyl) furan —(—CH═C(O—SiH—(CH₃)₂)—CH═C(O—SiH—(CH₃)₂)—O—)— cyclic 2,5-bis(dimethylsiloxanyl) furan —(—C(O—SiH—(CH₃)₂)═CH—CH═C(O—SiH—(CH₃)₂)—O—)— cyclic 1-dimethylsiloxanylfulvene —(—CH═CH—CH═CH—C(CH(O—SiH—(CH₃)₂))—)—, cyclic 2-dimethylsiloxanylfulvene —(—CH═CH—CH═CH—C(CH₂)(O—SiH—(CH₃)₂)—)—, cyclic 6-dimethylsiloxanylfulvene —(—C(O—SiH—(CH₃)₂)═CH—CH═CH—C═CH—)—, cyclic bis(dimethylsiloxanyl)fulvene (C₆H₄)(O—SiH—(CH₃)₂)₂, cyclic and fluorinated carbon derivatives thereof. Preferably the compounds are liquid at room temperature and can be volatilized near a pressure of 10 Torr or above. Such compounds react with an oxidizing gas to form a gel-like silicon/oxygen containing material that retains many of the labile organic groups at temperatures below about 50° C.

The amount of labile organic groups retained in the deposited silicon/oxygen containing material can be increased by mixing the reactive compounds with non-silicon containing components that comprise one or more labile organic groups. The labile organic groups include the dioxan, furan, and fulvene derivative chemicals described for the silicon containing reactive compounds and other oxygen containing organic groups. The labile organic groups are preferably the silicon containing and non-silicon containing components incorporated in the same molecule, but with the methylsilyl or methylsiloxanyl groups replaced with vinyl groups, or with the methylsiloxanyl groups replaced with ester groups, or with the methylsiloxanyl groups replaced with other non-silicon containing organic groups, in addition to those chemicals without the methylsiloxanyl groups, such as 1,4-dioxin and furan. Preferred non-silicon containing multiply unsaturated cycloalkanes (having two or more carbon-carbon double bonds) include: vinyl-1,4-dioxinyl ether CH₂═CH₂—O—(C₄H₃O₂), cyclic vinyl furyl ether CH₂═CH₂—O—(C₄H₃O), cyclic vinyl-1,4-dioxin CH₂═CH₂—(C₄H₃O₂), cyclic vinyl furan CH₂═CH₂—O—(C₄H₃O), cyclic methyl furoate CH₃C(O)—O—(C₄H₃O), cyclic furyl formate (C₄H₃O)—COOH, cyclic furyl acetate (C₄H₃O)—CH₂COOH, cyclic furaldehyde CH(O)—(C₄H₃O), cyclic difuryl ketone (C₄H₃O)₂C(O), cyclic difuryl ether (C₄H₃O)—O—(C₄H₃O), cyclic difurfuryl ether (C₄H₃O)C(O)—O—C(O)(C₄H₃O), cyclic furan, C₄H₄O, (cyclic) 1,4-dioxin, C₄H₄O₂, (cyclic) and fluorinated carbon derivatives thereof.

The non-silicon containing components can alternatively be mixed with the reactive silicon containing materials that do not contain labile organic groups, such as: methylsilane, CH₃—SiH₃ dimethylsilane, (CH₃)₂—SiH₂ disilanomethane, SiH₃—CH₂—SiH₃ bis(methylsilano)methane, CH₃—SiH₂—CH₂—SiH₂—CH₃ 2,4,6-trisilaoxane —(—SiH₂—CH₂—SiH₂—CH₂—SiH₂—O—)- (cyclic) 1,3,5-trisilacyclohexane, —(—SiH₂CH₂—)₃-(cyclic) cyclo-1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene —(—SiH₂—CH₂—SiH₂—O—)₂-(cyclic) 1,3-dimethyldisiloxane, CH₃—SiH₂—O—SiH₂—CH₃ 1,1,3,3-tetramethyldisiloxane (CH₃)₂—SiH—O—SiH—(CH₃)₂ 1,1,5,5-tetramethyltrisiloxane, and (CH₃)₂—SiH—O—SiH₂—O—SiH—(CH₃)₂ 1,1,3,5,5-pentamethyltrisiloxane (CH₃)₂—SiH—O—SiH(CH₃)—O—SiH—(CH₃)₂ and the fluorinated carbon derivatives thereof.

A combination of thermally-labile-imparting and non-thermally-labile-imparting compounds can be co-deposited to tailor film properties. A preferred embodiment of the co-deposition compounds include a thermally-labile-imparting compound selected from either methylsilyl-1,4-dioxinyl ether or 2-methylsiloxanyl furan and a non-thermally-labile-imparting compound selected from either 2,4,6-trisilaoxane (2,4,6-trisilatetrahydropyran) or cyclo-1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene.

The co-deposited heteroalicyclic non-thermally-labile imparting molecules which can be used advantageously are non-planar cyclic molecules with insignificant ring strain and which deposit in random orientations. For 2,4,6-trisilaoxane and cyclo-1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene, the dual bonding of the silyl functional groups to the methylene groups can provide improved thermal stability and better mechanical properties of the resultant film. The non-planar molecule can provide a relatively reduced stack density within the deposited film, thereby producing low dielectric films.

After the silicon/oxygen containing material is deposited as a film, the film is preferably annealed at a gradually increasing temperature to convert the labile organic groups to dispersed gas pockets in a nano-porous silicon oxide layer having a low dielectric constant attributed to a preferably closed cell foam structure.

In a preferred embodiment, the nano-porous silicon oxide layer of the present invention is deposited on a PECVD silicon oxide, silicon nitride, silicon oxynitride, or hydrogenated silicon carbide (e.g., BLOk™ layer material available from Applied Materials Inc., of Santa Clara, Calif.) barrier layer that was deposited on a patterned metal layer by plasma assisted reaction of one or more reactive silicon containing compounds. The nano-porous silicon oxide layer is then deposited in the same multichamber clustered CVD system while applying RF power or remote microwave power, and is subsequently heated using an increasing temperature profile, optionally to between about 350° C. to about 400° C. The nano-porous silicon oxide layer is optionally capped in the same chamber or in an adjacent cluster tool processing chamber used to deposit the barrier layer, for example with a hydrogenated silicon carbide (BLOk™). The liner and cap layers serve as barriers which protect the nano-porous silicon oxide layer.

Treatment of the porous silicon oxide layer with a hydrophobic-imparting chemical during or following curing at an elevated temperature, improves the moisture resistance of the deposited film. The chemical used is preferably selected from a group consisting of hexamethyldisilazane, trimethylsilyldiethylamine, phenyldimethylsilyldimethylamine, trimethoxysilyldi-methylamine, tris(trifluoromethyl)silyldimethylamine, bis(trimethyl-silyl)hydrazine, 1-phenyldimethylsilyl-2-methyl-hydrazine, 1-trimethoxysilyl-2-methyl-hydrazine, 1-tris(trifluoromethylsilyl)-2-methyl-hydrazine, trimethylchlorosilane, trimethylbromosilane, trimethylsilane, or combinations thereof.

The liner and cap layers can be deposited by plasma assisted chemical vapor deposition (CVD) of silicon oxide, silicon nitride, silicon oxynitride, or hydrogenated silicon carbide (BLOk™).

As described in detail below, the use of certain non-silicon-containing components may allow post-deposition residues to be more easily removed from the chamber by plasma cleaning.

Further description of the invention will be directed toward a specific apparatus for depositing nano-porous silicon oxide layers of the present invention.

Exemplary CVD Plasma Reactor

One suitable CVD plasma reactor in which a method of the present invention can be carried out is the “DLK” chamber available from Applied Materials of Santa Clara, Calif., and is shown in FIG. 2, which is a vertical, cross-section view of a parallel plate chemical vapor deposition reactor 110 having a high vacuum region 115. Reactor 110 contains a gas distribution manifold 111 for dispersing process gases through perforated holes in the manifold to a substrate or substrate (not shown) that rests on a substrate support plate or susceptor 112 which is raised or lowered by a lift motor 114. A liquid injection system (not shown), such as typically used for liquid injection of TEOS, may also be provided for injecting a liquid reactant. Preferred liquid injection systems include the AMAT Gas Precision Liquid Injection System (GPLIS) and the AMAT Extended Precision Liquid Injection System (EPLIS), both available from Applied Materials, Inc.

The reactor 110 includes heating of the process gases and substrate, such as by resistive heating coils (not shown) or external lamps (not shown). Referring to FIG. 2, susceptor 112 is mounted on a support stem 113 so that susceptor 112 (and the substrate supported on the upper surface of susceptor 112) can be controllably moved between a lower loading/off-loading position and an upper processing position which is closely adjacent to manifold 111.

When susceptor 112 and the substrate are in processing position 114, they are surrounded by a an insulator 117 and process gases exhaust into a manifold 124. During processing, gases inlet to manifold 111 are uniformly distributed radially across the surface of the substrate. A vacuum pump 132 having a throttle valve controls the exhaust rate of gases from the chamber.

Before reaching manifold 111, deposition and carrier gases are input through gas lines 118 into a mixing system 119 where they are combined and then sent to manifold 111. An optional microwave system 150 (shown in FIG. 3) having a applicator tube 120 may be located on the input gas line for the oxidizing gas to provide additional energy that dissociates only the oxidizing gas prior to entry to the reactor 110. The microwave applicator provides a power from between about 0 and about 6000 W. Generally, the process gases supply lines 18 for each of the process gases include (i) safety shut-off valves (not shown) that can be used to automatically or manually shut off the flow of process gas into the chamber, and (ii) mass flow controllers (also not shown) that measure the flow of gas through the gas supply lines. When toxic gases are used in the process, several safety shut-off valves are positioned on each gas supply line in conventional configurations.

The deposition process performed in reactor 110 can be either a non-plasma process on a cooled substrate pedestal or a plasma enhanced process. In a plasma process, a controlled plasma is typically formed adjacent to the substrate by RF energy applied to distribution manifold 111 from RF power supply 125 (with susceptor 112 grounded). Alternatively, RF power can be provided to the susceptor 112 or RF power can be provided to different components at different frequencies. RF power supply 125 can supply either single or mixed frequency RF power to enhance the decomposition of reactive species introduced into the high vacuum region 115. A mixed frequency RF power supply typically supplies power at a high RF frequency (RF1) of about 13.56 MHz to the distribution manifold 111 and at a low RF frequency (RF2) of about 360 KHz to the susceptor 112. The silicon oxide layers of the present invention are most preferably produced using low levels or pulsed levels of high frequency RF power. Pulsed RF power preferably provides 13.56 MHz RF power at about 20 to about 200 W during about 10% to about 30% of the duty cycle. Non-pulsed RF power preferably provides 13.56 MHz RF power at about 10 to about 150 W as described in more detail below. Low power deposition preferably occurs at a temperature range from about −20 to about 40° C. At the preferred temperature range, the deposited film is partially polymerized during deposition and polymerization is completed during subsequent curing of the film.

When additional dissociation of the oxidizing gas is desired, an optional microwave chamber can be used to input from about 0 to about 3000 W of microwave power to the oxidizing gas prior to entering the deposition chamber. Separate addition of microwave power would avoid excessive dissociation of the silicon compounds prior to reaction with the oxidizing gas. A gas distribution plate having separate passages for the silicon compound and the oxidizing gas is preferred when microwave power is added to the oxidizing gas.

Typically, any or all of the chamber lining, gas inlet manifold faceplate, support stem 113, and various other reactor hardware is made out of material such as aluminum or anodized aluminum. An example of such a CVD reactor is described in U.S. Pat. No. 5,000,113, entitled “Thermal CVD/PECVD Reactor and Use for Thermal Chemical Vapor Deposition of Silicon Dioxide and In-situ Multi-step Planarized Process,” issued to Wang et al. and assigned to Applied Materials, Inc., the assignee of the present invention.

The lift motor 114 raises and lowers susceptor 112 between a processing position and a lower, substrate-loading position. The motor, the gas mixing system 119, and the RF power supply 125 are controlled by a system controller 134 over control lines 136. The reactor includes analog assemblies, such as mass flow controllers (MFCs) and standard or pulsed RF generators, that are controlled by the system controller 134 which executes system control software stored in a memory 210, which in the preferred embodiment is a hard disk drive. Motors and optical sensors are used to move and determine the position of movable mechanical assemblies such as the throttle valve of the vacuum pump 132 and motor for positioning the susceptor 112.

The system controller 134 controls all of the activities of the CVD reactor and a preferred embodiment of the controller 134 includes a hard disk drive, a floppy disk drive, and a card rack. The card rack contains a single board computer (SBC), analog and digital input/output boards, interface boards and stepper motor controller boards. The system controller conforms to the Versa Modular Europeans (VME) standard which defines board, card cage, and connector dimensions and types. The VME standard also defines the bus structure having a 16-bit data bus and 24-bit address bus.

FIG. 3 is a simplified diagram of a remote microwave system 150 for dissociating process gases such as water prior to entering the DLK reactor 110, in accordance with an embodiment of the present invention. Remote microwave system 150 includes an applicator tube 120, a plasma ignition system including an ultraviolet (UV) lamp 154 and a UV power supply 155, a microwave waveguide system that includes various lengths of straight and curved waveguide sections 156, waveguide coupling 158, which may be connected together at joints 157, an output waveguide section 160, and a magnetron 168. The waveguide section 156 may further have an arm support 162 formed therein for attachment to an pivoting arm 164 mounted on a arm base 166. The pivoting arm comprises arm pieces 165 coupled to arm joints 163 that provide vertical separation of the arm pieces and allow rotational movement of the arm 164 around the arm joints 163. The arm joints 163, are vertically disposed cylinders coupled to one arm piece 165 at the bottom of the arm joint 163 and coupled to a second arm piece 165 at the top of the arm joint 165. The attachment of the arm pieces 165 at the ends of the arm joint 163 allow for vertical separation of the arm pieces and flexibility of position the arm 164, and thus the microwave system 150, during operation and maintenance of the processing reactor 110.

Magnetron 168 is a typical magnetron source capable of operating between about 0-3000 Watts for continuous wave (CW) or pulsed output of microwaves of about 2.45 Gigahertz (GHz) frequency. Of course, other magnetrons may be utilized as well. Circulator (not shown) allows only forward microwave transmission from magnetron 168 toward applicator tube 120. Tuning system 170, which may use stub tuners or other tuning elements, provides the microwave system 150 with the ability to match the load at waveguide section 160 to the characteristic impedance of the waveguides. Tuning system 170 may provide fixed tuning, manual tuning, or automated tuning, according to specific embodiments. In the specific embodiment, the waveguide sections have rectangular cross-sections, but other types of waveguide also may be used.

Applicator tube 120 is a circular (or other cross-section) tube made of a composite or ceramic material, preferably alumina, or other material resistant to etching by radicals. In a specific embodiment, applicator tube 120 has a length of about 18-24 inches and a cross-sectional diameter of about 3-4 inches. Applicator tube 120 is disposed through a waveguide section 160, which is open at one end for transmitting microwaves and is terminated at the other end with a metal wall. Microwaves are transmitted through the open end of waveguide section 160 to gases inside applicator tube 120, which is transparent to microwaves. Of course, other materials such as sapphire also may be used for the interior of applicator tube 120. In other embodiments, applicator tube 120 may have a metal exterior and an interior made of a composite or ceramic material wherein microwaves in waveguide section 160 enter a window through the exterior of applicator tube 120 to the exposed interior of tube 120 to energize the gases.

The above-described method can be implemented in a system that is controlled by a processor based system controller such as the controller 134 shown in FIG. 2. FIG. 4 shows a block diagram of a processing system, or reactor 110, such as that depicted in FIG. 2, having such a system controller 134 that can be employed in such a capacity. The system controller 134 includes a programmable central processing unit (CPU) 220 that is operable with a memory 210, a mass storage device 215, an input control unit 245, and a display unit 255. The system controller further includes well-known support circuits 214 such as power supplies, clocks 225, cache 235, input/output (I/O) circuits 240 and the like, coupled to the various components of the DLK process reactor 110 to facilitate control of the deposition process. The controller 134 also includes hardware for monitoring substrate processing through sensors (not shown) in the chamber 110. Such sensors measure system parameters such as substrate temperature, chamber atmosphere pressure and the like. All of the above elements are coupled to a control system bus 230.

To facilitate control of the chamber as described above, the CPU 220 may be one of any form of general purpose computer processor that can be used in an industrial setting for controlling various chambers and subprocessors. The memory 210 is coupled to the CPU 220, and is accessible to the system bus 230. The memory 210, or computer-readable medium 215, may be one or more of readily available memory such as random access memory (RAM), read only memory (ROM), floppy disk drive, hard disk, or any other form of digital storage, local or remote. The support circuits 214 are coupled to the CPU 220 for supporting the processor in a conventional manner. The deposition process is generally stored in the memory 210, typically as a software routine. The software routine may also be stored and/or executed by a second CPU (not shown) that is remotely located from the hardware being controlled by the CPU 220.

The memory 210 contains instructions that the CPU 220 executes to facilitate the performance of the processing system 10. The instructions in the memory 210 are in the form of program code such as a program 200 that implements the method of the present invention. The program code may conform to any one of a number of different programming languages. For example, the program code can be written in C, C++, BASIC, Pascal, or a number of other languages.

The mass storage device 215 stores data and instructions are retrieves data and program code instructions from a processor readable storage medium, such as a magnetic disk or magnetic tape. For example, the mass storage device 215 can be a hard disk drive, floppy disk drive, tape drive, or optical disk drive. The mass storage device 215 stores and retrieves the instructions in response to directions that it receives from the CPU 220. Data and program code instructions that are stored and retrieved by the mass storage device 215 are employed by the processor unit 220 for operating the processing system. The data and program code instructions are first retrieved by the mass storage device 215 from a medium and then transferred to the memory 210 for use by the CPU 220.

The input control unit 245 couples a data input device, such as a keyboard, mouse, or light pen, to the processor unit 220 via the system bus 230 to provide for the receipt of a chamber operator's inputs. The display unit 255 provides information to a chamber operator in the form of graphical displays and alphanumeric characters under control of the CPU 220.

The control system bus 230 provides for the transfer of data and control signals between all of the devices that are coupled to the control system bus 230. Although the control system bus is displayed as a single bus that directly connects the devices in the CPU 220, the control system bus 230 can also be a collection of busses. For example, the display unit 255, input control unit 245 (with input device), and mass storage device 215 can be coupled to an input-output peripheral bus, while the CPU 220 and memory 210 are coupled to a local processor bus. The local processor bus and input-output peripheral bus are coupled together to form the control system bus 230.

The system controller 134 is coupled to the elements of the processing system 10, employed in dielectric deposition processes in accordance with the present invention via the system bus 230 and the I/O circuits 240. The I/O circuits 240 receive instructions from the program 200 stored in memory 210 via the CPU 220 and system bus 230. The program 200 provides program subroutines that enable the I/O circuits 240 to provide for substrate positioning control 250, process gas control 260, pressure control 270, heater control 280, and plasma/microwave control 290, of the reactor 110.

The CPU 220 forms a general purpose computer that becomes a specific purpose computer when executing programs such as the program 200 of the embodiment of the method of the present invention depicted in the flow diagram of FIG. 4. Although the invention is described herein as being implemented in software and executed upon a general-purpose computer, those skilled in the art will realize that the invention could be implemented using hardware such as an application specific integrated circuit (ASIC) or other hardware circuitry. As such, it should be understood that the invention can be implemented, in whole or in part, in software, hardware or both.

The above CVD system description is mainly for illustrative purposes, and other plasma CVD equipment such as electrode cyclotron resonance (ECR) plasma CVD devices, induction-coupled RF high density plasma CVD devices, or the like may be employed. Additionally, variations of the above described system such as variations in susceptor design, heater design, location of RF power connections and others are possible. For example, the substrate could be supported and heated by a resistively heated susceptor. The pretreatment and method for forming a pretreated layer of the present invention is not limited to any specific apparatus or plasma excitation method.

Deposition of a Nano-Porous Silicon Oxide Layer

The nano-porous silicon oxide layer of the present invention can be deposited in a three-layer process as shown in FIG. 5 using the PECVD or microwave chamber of FIG. 2. Referring to FIG. 5, a substrate is positioned 300 in the reactor 110 and a barrier layer is deposited 305 by a PECVD process from a plasma comprising a reactive silicon containing compound. The deposition step 305 can include a capacitively coupled plasma or both an inductively and a capacitively coupled plasma in the process chamber 15 according to methods known in the art. An inert gas such as helium is commonly used in the PECVD deposition to assist in plasma generation. A nano-porous layer of the present invention is then deposited 310 on the liner layer by depositing a silicon/oxygen containing material that further contains labile organic groups, and by controlled annealing of the deposited silicon/oxygen containing material to form microscopic gas pockets that are uniformly dispersed in the layer. Carbon doped oxide (CDO) films, also referred as silicon oxides (SiCOH), are examples of such silicon/oxygen containing materials. A carbon-containing precursor having labile organic groups is also incorporated into the nano-porous layer, which is later removed to create porosity. Such examples of carbon-containing precursors are limonene, carene, cymene, and fenchone. Next, a cap layer is then deposited 315 on the layer, preferably using a similar process as employed for depositing the lining layer. The substrate is then removed 320 from the reactor 110.

Following deposition, the chamber may be cleaned to remove any residues remaining on chamber components that could potentially contaminate incoming wafers subjected to processing. Accordingly, in step 322, a highly reactive species such as fluorine radicals and fluorine ions are introduced into the deposition chamber. These reactive species may result from a plasma generated in-situ or generated remotely and then flowed into the deposition chamber.

Ordinarily, these reactive species consume any residue remaining from the prior steps of depositing and curing the nanoporous material. However, the use of certain organic compounds during the deposition process results in the formation of reaction or decomposition by-products in the processing chamber that are difficult to remove using conventional in situ cleaning methods. In other instances, reaction by-products may be converted to residue by in situ cleaning that cannot readily be removed.

The process of annealing the deposited film to release the thermally labile groups of the silicon/oxygen containing material, creates reaction by-products within the reactor. These reaction by-products can remain within the reactor and serve as a source of contamination for processing of additional substrates. Accordingly, in step 325, the empty reactor 110 is periodically exposed to a dry cleaning step, with reactive species flowed in from the microwave system 150 shown in FIG. 3.

The dry cleaning process of step 325 is effective to remove many of the residues built up in the reactor during processing. However, in order to ensure full cleaning of the chamber, at a less frequent interval, the reactor is exposed to a wet cleaning step 326. During this wet clean, the interior of the reactor is exposed to etchants in liquid form, such as halogen-containing etching chemicals.

FIGS. 9A-B show photographs taken of a 300 mm BDIIx chamber after running a diethoxymethyl silane (DEMS)+alpha-terpentine (ATRP: 1-methyl-4-(1-methylethyl)-1,3-cyclohexadiene) deposition process followed by plasma cleaning using a standard NF₃ remote plasma system (RPS)—only clean. Two types of residue were found.

FIG. 9A shows a photograph of a deposition chamber surface bearing a wax residue following attempted in-situ cleaning. FIG. 9B shows a photograph of a deposition chamber surface bearing a powder residue following attempted in-situ cleaning. FIGS. 9C and 9D are Fourier-Transfer Infra-Red (FT-IR) spectra showing absorbance of the wax and powder residues of FIGS. 9A-B.

The first residue shown in FIG. 9A was a powder comprising mainly CFx groups. This powder is believed to be a by-product of the reaction between fluorine in the cleaning gas, and ATRP by-products.

The second residue shown in FIG. 9B is a waxy substance. The FT-IR analysis of this residue showed it to be organic in nature and comprising mainly of a cross-linked polymer with low molecular weight poly-methylene chains.

The first, powdery residue may cause particle contamination. The second, waxy residue accumulates in certain areas of the chamber, thereby lessening the number of substrates which can be processed between the periodic wet chamber cleaning steps. The presence of either residue type renders problematic any development of a manufacturable process using ATRP.

Accordingly, embodiments of the present invention utilize a process for forming nanoporous materials that are more “cleanable.” TABLE 2 below lists several such pore forming chemicals that may be utilized as an alternative to ATRP. TABLE 2 NON-SILICON CONTAINING COMPONENT (LARGE POROGEN) Molecular CAS Reg. Chemical Name Formula Weight No. Structure 1-methyl-4-(1- C₁₀H₁₄ 134.22 99-87-6 methylethyl)-Benzene (“Cymene”) 3-Carene C₁₀H₁₆ 136.23 13466-78-9 Fenchone C₁₀H₁₆O 152.23 126-21-6 Limonene C₁₀H₁₆ 136.23 138-86-3 Vinyl acetate C₄H₆O₂ 89.09 108-05-4 Methyl methacrylate C₅H₈O 100.12 80-62-6 Ethyl vinyl ether C₄H₈O 72.11 109-92-2 Tetrahydrofuran C₄H₈O 72.11 109-99-9 Furan C₄H₄O 68.08 110-00-9 2,5 Norbornadiene C₇H₈ 92.14 121-46-0 Cyclopentene C₅H₈ ˜68 142-29-0 Cyclopentene oxide C₅H₈O 84.12 285-67-6 Methyl cyclopentene C₆H₁₀ 82.15 693-89-0 2-cyclopentene-1-one C₅H₈O 82.1 930-30-3 1-butene C₄H₈ ˜56 25167-67-3

By utilizing the alternative pore-forming materials listed in TABLE 2 and illustrated in FIGS. 10A-D, formation of the difficult-to-remove wax residue may be avoided. In addition, the absence of ATRP may suppress formation of the powder-type residue resulting from interaction between the ATRP and the cleaning plasma.

Returning now to the description of a damascene process utilizing nanoporous low K materials, FIGS. 6A-6E show that a the three-layer process provides a PECVD lining layer 400. The lining layer 400 acts as an isolation layer between the subsequent nano-porous layer 402 and the underlying substrate surface 404 and metal lines 406, 408, 410 formed on the substrate surface. The nano-porous layer 402 is capped by a PECVD capping layer 412 of the silicon containing compound. This process is implemented and controlled using a computer program stored in the memory 220 of a computer controller 134 for a CVD reactor 110.

Referring to FIG. 6A, the PECVD lining layer 400 is deposited in the reactor 110 by introducing a reactive silicon containing compound and an oxidizing gas. The process gases react in a plasma enhanced environment to form a conformal silicon oxide layer 400 on the substrate surface 404 and metal lines 406, 408, 410.

Referring to FIG. 6B, the nano-porous layer 402 is deposited from a processing gas consisting of silicon and labile containing compounds and an oxidizing gas. The process gas flows range from about 20 to about 1000 sccm for the silicon and labile containing compounds, and about 5 to about 4000 sccm of the oxidizing gas. The preferred gas flows range from about 50 to about 500 sccm for the silicon and labile containing compounds and a flow rate of about 5 to about 2000 sccm of the oxidizing gas. These flow rates are given for a chamber having a volume of approximately 5.5 to 6.5 liters. Preferably, reactor 110 is maintained at a pressure of about 0.2 to about 5 Torr during deposition of the nano-porous layer 402. The nano-porous layer 402 is cured as shown in FIG. 6C to remove volatile constituents prior to deposition of a cap layer 412 as shown in FIG. 6D. Curing can be performed in the reactor 110 under an inert gas atmosphere while heating the substrate to progressively higher temperatures.

The nano-porous layer 402 is preferably annealed at a gradually increasing temperature to retain gaseous products as dispersed microscopic bubbles, and/or to convert the optional labile organic groups to dispersed microscopic gas bubbles that are retained in the cured silicon oxide film as voids in a preferably closed cell structure. A preferred anneal process comprises a heating time period of about 5 minutes, including gradually raising the temperature by about 50° C./min to a final temperature of between about 350° C. to about 400° C. Dispersion of the gas bubbles can be controlled by varying the temperature/time profile and by controlling the concentration of labile organic groups in the deposited film.

Referring to FIG. 6D, the reactor 110 deposits a capping layer 412, preferably of the same material and by the same methods as used for the deposition of the PECVD liner layer 400. Referring to FIG. 6E, after deposition of the capping layer 412, the deposited layers are further annealed in a furnace or another chamber at a temperature from about 200° C. to about 450° C. to drive off remaining volatile products such as water. Of course, processing conditions will vary according to desired characteristics of the deposited films.

Deposition of a Dual Damascene Structure

A preferred dual damascene structure 500 fabricated in accordance with the invention is shown in FIG. 7, and the method of making the structure is sequentially depicted schematically in FIGS. 8A-8H, which are cross sectional views of a substrate having the steps of the invention formed thereon.

A dual damascene structure 500 which includes a nano-porous intermetal dielectric layer 510 is shown in FIG. 7. The intermetal dielectric layers 510 and 514 deposited according to the invention have extremely low dielectric constants of less than 3, and are often referred to as extreme low k, or ELk, dielectric layers. A first dielectric layer 510, preferably consisting of the nano-porous silicon oxide layer of the present invention is deposited on a substrate 502. The substrate comprising patterned conducting lines 506 formed in a contact level substrate material 504, with a first (or substrate) etch stop 508 of silicon oxide, silicon nitride, silicon oxynitride, or amorphous hydrogenated silicon carbide (BLOk™), preferably silicon nitride, deposited thereon.

A silicon oxide, silicon nitride, silicon oxynitride, or hydrogenated silicon carbide (BLOk™) second etch stop 512 is deposited on the first dielectric layer 510. A second dielectric layer 514, preferably consisting of the nano-porous silicon oxide layer of the present invention is deposited on the second etch stop 512, with a third etch stop 516 deposited on the second dielectric layer 514. The deposited layers are etched to form a via 520, which is subsequently filled with a conducting metal 524, preferably copper, over a barrier layer 522 conformally deposited within the via 520. The structure is then planarized and a capping layer 518 comprising silicon nitride, silicon oxide, silicon oxynitride, or hydrogenated silicon carbide, preferably comprising silicon nitride, is deposited thereon. The capping layer 518 also serves as the substrate etch stop and corresponds to the first etch stop 508 for subsequent dual damascene multilevel interconnects.

As shown in FIG. 8A, a first (or substrate) etch stop 508 of silicon oxide, silicon nitride, silicon oxynitride, or amorphous hydrogenated silicon carbide, preferably silicon nitride is deposited to a thickness of about 1000 Å on the substrate 502. The substrate 502 comprises patterned conducting interconnects or lines 506 formed in a contact level substrate material 504. A first nano-porous dielectric layer 510 is deposited according to the invention on the first etch stop 508. The first dielectric layer 510 has a thickness of about 5,000 Å to about 10,000 Å, depending on the size of the structure to be fabricated, but has a preferable thickness of about 5,000 Å. The first dielectric layer 510 and is then annealed at a temperature of about 350° C. to about 400° C. to remove volatile contaminants from the layer 510. A second etch stop 512, such as silicon oxynitride, is deposited on the dielectric layer 510 to a thickness of about 500 Å. A second nano-porous dielectric layer 514 is then deposited a thickness of about 5,000 Å to about 10,000 Å preferably about 5,000 Å, according to the invention on the first etch stop 508, and is then annealed at a temperature of about 350° C. to about 400° C.

A third etch stop 516 of silicon oxide, silicon nitride, silicon oxynitride, or amorphous hydrogenated silicon carbide (BLOk™), preferably silicon nitride is deposited on the second dielectric layer 514 to a thickness of about 500 Å to about 1000 Å, preferably at about 1000 Å. A silicon oxide layer 517 having a thickness of about 2000 Å is the deposited on the third etch stop 516 to serve both as a hard etch mask as well as for future use in a chemical mechanical polishing (CMP) step. An anti-reflective coating (ARC) 519 and a trench photomask comprising a photoresist layer 521 are then respectfully deposited over the silicon oxide layer 517. The photoresist layer 521 is then patterned by conventional photolithography means known in the art.

The silicon oxide layer 517 is then etched by conventional means known in the art, preferably by an etch process using fluorocarbon chemistry, to expose the third etch 516 as shown in FIG. 8B. The initial etch of the silicon oxide layer 517 establishes the opening width, or trench width, of the dual damascene structure 500. The opening width formed in the silicon oxide layer 517 defines the horizontal interconnect of the dual damascene structure 500 formed above the second etch stop 514. The remaining photoresist 521 is then ashed, or dry removed, for preparation of the via etch. For formation of the contact or via width of the dual damascene structure, a second anti-reflective coating 519 and a photoresist layer 521 are then respectfully deposited over the thin silicon oxide layer 517, and then patterned by photolithography to expose the third etch layer 516 by the via width as shown in FIG. 8C.

Referring to FIG. 8D, the third etch stop 516 and second dielectric layer 514, are trenched etched to expose the second etch stop 512. The via 520 is then formed by via etching the second dielectric layer 514 to the second etch stop 512 using anisotropic etching techniques to define the metallization structure (i.e., the interconnect and contact/via) at the width established by the silicon oxide layer 517; and etching the first dielectric layer 510 to the first etch stop 508 at the via width established during the etching of the third etch stop 516, second dielectric layer 514, and the second etch stop 512 as shown in FIG. 8E. Any photoresist or ARC material used to pattern the second etch stop 512 or the second dielectric layer 514 is removed using an oxygen strip or other suitable process. FIG. 8F shows the etching of the first etch stop 508 protecting the substrate 502, exposing the underlying patterned metal lines 506 in the contact level substrate material 504. The patterned metal lines 506 preferably comprise a conducting metal such as copper. The dual damascene structure 500 is then precleaned by conventional means known in the art prior to subsequent layer deposition.

The metallization structure is then formed with a conductive material such as aluminum, copper, tungsten or combinations thereof. Presently, the trend is to use copper to form the smaller features due to the low resistivity of copper (1.7 mW-cm compared to 3.1 mW-cm for aluminum). Preferably, as shown in FIG. 8G, a suitable barrier layer 522 such as tantalum nitride is first deposited conformally in the metallization pattern 520 to prevent copper migration into the surrounding silicon and/or dielectric material. Thereafter, a layer of copper 524 is deposited using either chemical vapor deposition, physical vapor deposition, electroplating, preferably by electroplating, to form the conductive structure. Once the structure has been filled with copper or other metal, the surface is planarized using chemical mechanical polishing and capped with a capping layer 518, preferably comprising silicon nitride and having a thickness of about 1000 Å, as shown in FIG. 8H. Prior to planarizing the surface, the metal may be annealed in a hydrogen atmosphere to recrystallize the copper fill and to remove voids that may have formed in the structure 500. While not shown, a copper seed layer may be deposited prior to the copper layer 524 when the copper layer 524 is deposited by an electroplating process. The dual damascene formation process may then be repeated to deposit further interconnection levels, of which modern microprocessor integrated circuits have 5 or 6 interconnection levels.

EXAMPLES

The following examples demonstrate deposition of a nano-porous silicon oxide based film having dispersed microscopic gas voids. This example is undertaken using a chemical vapor deposition chamber, and in particular, a CENTURA “DLK” system fabricated and sold by Applied Materials, Inc., Santa Clara, Calif.

Silicon Compound Having Silicon Containing and Thermally Labile Imparting Components (Hypothetical)

A nano-porous silicon oxide based film is deposited at a chamber pressure of 1.0 Torr and temperature of 30° C. from reactive gases which are vaporized and flown into the reactor as follows: methylsilyl-2-furyl ether, at  150 sccm nitrous oxide (N₂O), at 1000 sccm

Prior to entering the chamber, the nitrous oxide is dissociated in a microwave applicator that provides 2000 W of microwave energy. The substrate is positioned 600 mil from the gas distribution showerhead and the reactive gases are introduced for 2 minutes. The substrate is then heated over a time period of 5 minutes, raising the temperature of the substrate by 50° C./min to a temperature of 400° C. to cure and anneal the nano-porous silicon oxide based film.

Mixture of Silicon Containing Compound And Added Thermally Labile Imparting Compound (Hypothetical)

A nano-porous silicon oxide based film is deposited at a chamber pressure of 1.0 Torr and temperature of 30° C. from reactive gases which are vaporized and flown into the reactor as follows: cyclo-1,3,5,7-tetrasilylene-2,6-dioxy-4,8 dimethylene, at  100 sccm vinyl-2-furyl ether, at  50 sccm Nitrous Oxide (N₂O), at 1000 sccm

Prior to entering the chamber, the nitrous oxide is dissociated in a microwave applicator that provides 2000 W of microwave energy. The substrate is positioned 600 mil from the gas distribution showerhead and the reactive gases are introduced for 2 minutes. The substrate is then heated over a time period of 5 minutes, raising the temperature of the substrate by 50° C./min to a temperature of 400° C. to cure and anneal the nano-porous silicon oxide based film.

Silicon Compound Having Silicon Containing and Thermally Labile Imparting Components And Added Silicon Containing Compound (Hypothetical)

A nano-porous silicon oxide based film is deposited at a chamber pressure of 1.0 Torr and temperature of 0° C. from reactive gases which are vaporized and flown into the reactor as follows: methylsilyl-2-furyl ether, at 100 sccm cyclo-1,3,5,7-tetrasilylene-2,6-dioxy-4,8 dimethylene, at  50 sccm Nitrous Oxide (N₂O), at 1000 sccm. 

Prior to entering the chamber, the nitrous oxide is dissociated in a microwave applicator that provides 2000 W of microwave energy. The substrate is positioned 600 mil from the gas distribution showerhead and the reactive gases are introduced for 2

/minutes. The substrate is then heated over a time period of 5 minutes, raising the temperature of the substrate by 50° C./min to a temperature of 400° C. to cure and anneal the nano-porous silicon oxide based film.

While the above is a complete description of specific embodiments of the present invention, various modifications, variations, and alternatives may be employed. These equivalents and alternatives are included within the scope of the present invention. Therefore, the scope of this invention is not limited to the embodiments described, but is defined by the following claims and their full scope of equivalents. 

1. A method for generating a low dielectric constant film, comprising: disposing a substrate within a processing chamber; providing an oxidizable silicon containing compound into the processing chamber; providing a carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, 2,5 Norbornadiene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene into the processing chamber; reacting the oxidizable silicon containing compound and the carbon containing precursor with an oxidizing gas to form a carbon-doped dielectric film over the substrate; and annealing the substrate to create pores in the carbon-doped dielectric film.
 2. The method of claim 1 wherein the substrate is annealed to a final temperature of between about 350° C. to about 400° C.
 3. The method of claim 1 further comprising: removing the substrate from the processing chamber after annealing; and cleaning the vacant processing chamber by exposure to halogen ions.
 4. The method of claim 3 wherein the halogen ions comprise a plasma generated within the processing chamber.
 5. The method of claim 3 wherein the halogen ions are generated remote from the processing chamber and then flowed into the processing chamber.
 6. The method of claim 3 wherein the halogen ions comprise fluorine.
 7. The method of claim 1 wherein the annealing releases a thermally labile group comprising a cyclodialkene.
 8. The method of claim 1 wherein: the carbon doped silicon oxide film is deposited over a first etch stop on the substrate; and wherein the method further comprises, depositing a second etch stop on the annealed carbon-doped silicon oxide layer; depositing a second carbon-doped silicon oxide layer on the second etch stop by oxidative reaction between a second oxidizable silicon containing component and a second carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, bicyclo-hepa-diene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene; annealing the second carbon-doped silicon oxide layer to form pores therein; depositing a third etch stop on the second silicon oxide based layer; etching the third etch stop and the second silicon oxide layer to define an opening; and etching the second etch stop, the first silicon oxide layer, and the first etch stop through the opening to form a via.
 9. The method of claim 8 further comprising depositing metal within the via to form a dual damascene structure.
 10. The method of claim 1 wherein providing the oxidizable silicon-containing compound further comprises providing at least one of octamethyl-trisiloxane, 1,1,1,3,5,5,5,-heptamethyl-trisiloxane, 1,3,5-trimethyl-1,3,5-trivinylcyclotrisiloxane, (CH₃)₂SiH)₂O, decamethylcyclopentasiloxane, 2,4,6,8-tetramethylcyclotetrasiloxane, octamethyl-cyclotetrasiloxane, methyldiethoxysilane, trimethyl-silane, and triethoxymethyl-silane.
 11. A dielectric structure for a semiconducting device comprising: a carbon-doped silicon oxide feature formed by the oxidative reaction between an oxidizable silicon containing compound and a carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, 2,5 Norbornadiene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene, followed by annealing to create pores therein.
 12. The dielectric structure of claim 11 further comprising a thermally labile group comprising a cyclodialkene.
 13. The dielectric structure of claim 11 selected from the group consisting of a shallow trench isolation structure, a pre-metal dielectric layer, and an intermetal dielectric layer.
 14. The dielectric structure of claim 11 formed by reaction of the silicon containing precursor selected from the group comprising octamethyl-trisiloxane, 1,1,1,3,5,5,5,-heptamethyl-trisiloxane, 1,3,5-trimethyl-1,3,5-trivinylcyclotrisiloxane, (CH₃)₂SiH)₂O, decamethylcyclopentasiloxane, 2,4,6,8-tetramethylcyclotetrasiloxane, octamethyl-cyclotetrasiloxane, methyldiethoxysilane, trimethyl-silane, and triethoxymethyl-silane.
 15. An apparatus for depositing a carbon-doped low K dielectric film, the apparatus comprising: a chamber enclosing a substrate support; a heat source in thermal communication with the chamber; an oxidizable silicon containing component source in fluid communication with the chamber; a carbon-containing precursor source in fluid communication with the chamber; an oxidant source in fluid communication with the chamber; a host processor in communication with the chamber; and a computer readable storage medium having a computer readable program embodied therein for directing operation of the processor to, cause the oxidizable silicon containing component to flow into the processing chamber, cause the carbon-containing precursor comprising at least one of limonene, carene, cymene, fenchone, vinyl acetate, methyl methacrylate, ethyl vinyl ether, tetrahydrofuran, furan, 2,5 Norbornadiene, cyclopentene, cyclopentene oxide, methyl cyclopentene, 2-cyclopentene-1-one, and 1-butene to flow into the processing chamber; cause the oxidant to flow into the chamber and react with the oxidizable silicon containing compound and the carbon containing precursor to form a carbon-doped dielectric film over a substrate supported by the support, and cause the heat source to anneal the substrate to create pores in the carbon-doped dielectric film.
 16. The apparatus of claim 15 wherein the computer readable program is configured to direct the heat source to anneal the substrate to a final temperature of between about 350° C. to about 400° C.
 17. The apparatus of claim 15 wherein the computer readable program is configured to expose the processing chamber to halogen ions following removal of the substrate.
 18. The apparatus of claim 15 further comprising an rf energy source in energetic communication with the processing chamber, wherein the computer readable program is configured to direct the rf energy source to generate a plasma containing the halogen ions within the processing chamber.
 19. The apparatus of claim 15 further comprising: a remote plasma system in fluid communication with the processing chamber; a halogen gas source in fluid communication with the remote plasma system; and an rf energy source in energetic communication with the remote plasma chamber, wherein the computer readable program is configured to direct the halogen gas source to flow halogen gas into the remote plasma system, to direct the rf energy source to generate a plasma containing the halogen ions within the remote plasma system, and to flow the halogen ions into the processing chamber. 